[1]吴 忠,戴 健,朱炳喜.新孟河界牌水利枢纽工程高性能混凝土应用实践[J].江苏水利,2020,(11):25-31+34.
　WU Zhong,DAI Jian,ZHU Bingxi.Application on practice of high performance concrete in Jiepai water conservancy project of Xinmeng River[J].JIANGSU WATER RESOURCES,2020,(11):25-31+34.
点击复制

新孟河界牌水利枢纽工程高性能混凝土应用实践()
分享到：

《江苏水利》[ISSN:1006-6977/CN:61-1281/TN]

卷:
期数:
2020年11期
页码:
25-31+34
栏目:
水利工程管理
出版日期:
2020-11-26

文章信息/Info

Title:
Application on practice of high performance concrete in Jiepai water conservancy project of Xinmeng River
文章编号:
1007-7839(2020)11-0025-07
作者:
吴 忠1;  戴 健1; 2;  朱炳喜3
1.江苏省新孟河枢纽工程建管局, 江苏 常州 213000; 2.江苏省太湖地区水利工程管理处, 江苏 苏州 215000; 3.江苏省水利科学研究院, 江苏 扬州 225002
Author(s):
WU Zhong1;  DAI Jian1; 2;  ZHU Bingxi3
1.Jiangsu New Menghe Junction Project Construction Management Bureau, Changzhou 213000, China; 2.Taihu Lake Region Hydraulic Project Management Division of Jiangsu Province, Suzhou 215000, China; 3.Jiangsu Institute of Water Resources and Hydropower Research, Yangzhou 225002, China
关键词:
高性能混凝土;  配合比;  质量控制;  高性能混凝土评价;  界牌水利枢纽
Keywords:
high performance concrete;  mixture ratio;  quality control;  evaluation of high performance concrete;  Jiepai water conservancy project
分类号:
TV431
文献标志码:
A
摘要:
新孟河延伸拓浚工程界牌水利枢纽工程设计使用年限为100年,主体结构混凝土设计指标为C30F50W6,服役期间主要受到碳化等腐蚀作用。施工过程中混凝土采用优选原材料、优化配合比、低用水量、低水胶比、较低的水泥用量、双掺粉煤灰与矿渣粉、掺聚羧酸高性能减水剂,矿物掺合料掺量中等偏上的配制技术,同时适当延长带模养护时间,闸墩和站墩通水冷却等施工技术措施防止产生温度裂缝。实施效果表明混凝土各项性能满足百年寿命混凝土的性能指标要求; 经设计、生产和实体结构质量3个方面评价,混凝土实现高性能化。
Abstract:
The design service life of Jiepai water control project of Xinmeng River extension dredging project is 100 years. The design index of main structure concrete was C30F50W6, and it was mainly subjected to carbonization and other corrosion during its service. During the construction process, compounding technologies of concrete adopted optimized raw materials, optimized mix ratio, low water consumption, low water-binder ratio, low cement consumption, double-mixed fly ash and slag powder, high-performance water reducing agent mixed with polycarboxylic acid, and mineral admixture with medium and higher dosage. The maintenance time of the belt mold was appropriately extended at the same time, and the construction technical measures such as water cooling of the gate pier and the station pier to prevent temperature cracks. The implementation results showed that the concrete performances could meet the requirement of performance index of hundred-year-old concrete. Through the evaluation of design, production and solid structure quality, concrete achieved high performance.

参考文献/References:

[1] 中华人民共和国行业标准. 水利水电工程合理使用年限及耐久性设计规范(SL654-2014)[S]. 北京:中国水利水电出版社, 2014.
[2] 住房和城乡建设部标准定额司, 工业和信息化部原材料工业司. 高性能混凝土应用技术指南[M]. 北京:中国建筑工业出版社, 2015.
[3] 中华人民共和国行业推荐性标准. 公路桥涵施工技术规范(JTG/T F 50-2011)[S]. 北京:人民交通出版社, 2011.
[4] 江苏省工程建设标准. 城市轨道交通工程高性能混凝土质量控制技术规程(DGJ32/T J 206-2016)[S]. 南京:江苏凤凰科学技术出版社, 2016.
[5] 朱炳喜. 试论沿海水工建筑物低渗透高密实表层混凝土施工质量控制要点[J]. 江苏水利, 2017(11):1-8.
[6] 江苏省质量技术监督局. 水利工程混凝土耐久性技术规范(DB32/T 2333-2013)[S]. 南京:江苏人民出版社, 2013(9).
[7] 江苏省水利科学研究院. 水利工程应用预拌混凝土高性能化后评价方法[R]. 南京:江苏省水利科学研究院, 2019.

备注/Memo

备注/Memo:
收稿日期:2020-08-13
基金项目:江苏省水利科技项目(2018013)
作者简介:吴忠(1969—),男,高级工程师,本科,主要从事水利工程建设管理工作。
通信作者:朱炳喜(1966—),男,研究员级高级工程师,工程硕士,硕士生导师,主要从事提升混凝土质量施工技术研究与应用。E-mail:1146513595@qq.com
更新日期/Last Update: 2020-11-20